Product parameters
Mechanical performance rating unit test method
Rockwell hardness 72.2 ASTM d785
Bending strength 86.6 MPa ASTM D790, ISO178
Bending modulus: 2087 MPa (ASTM D790 / ISO178)
Tensile strain
Fracture 148.1% ASTM D638, iso527
Tensile strength 60.7 MPa ASTM D638, iso527
Unit test method for impact performance rating
Charpy Notched Impact Strength
23°C 20.1 J/m ASTM D256 , ISO179
Physical performance rating unit test method
Water absorption
23°C/24H <0.07 % ASTM D570, ISO62
Melt mass flow rate
200°C, 5.0kg 2.85 g/10min ASTM D1238 , ISO1133
Shrinkage: 0.93%, ASTM D955
Density 1.156 g / cm3 ASTM D792, iso1183
Thermal performance rating unit test method
Melting point: 215-220 ° C-
Thermal deformation temperature
UN annealed 71 ° C ASTM D648, iso75
Electrical performance rating unit test method
Surface resistivity 2.4e + 13 ohms ASTM D257, IEC60093
Volume resistivity 1.5x10a14 ohms cm ASTM D257, IEC60093
Dielectric constant
1 MHz 0.65 ASTM D150, IEC60250
Application
The chemical and physical properties of PA6 are similar to those of PA66. However, its melting point is low and the process temperature range is wide. Its impact resistance and solubility are better than PA66, but its moisture absorption is also stronger. Because many quality characteristics of plastic parts are affected by moisture absorption, this should be fully considered when using PA6 to design products. In order to improve the mechanical properties of PA6, various modifiers are often added. Glass fiber is the most common additive. Sometimes synthetic rubber, such as EPDM and SBR, is added to improve impact resistance. For products without additives, the shrinkage of PA6 is between 1% and 1.5%. Adding glass fiber additives can reduce the shrinkage to 0.3% (but it is slightly higher in the direction perpendicular to the process). The shrinkage of molding assembly is mainly affected by the crystallinity and moisture absorption of the material. The actual shrinkage is also a function of the plastic part design, wall thickness and other process parameters.
PA6 nylon is widely used in the industrial production of bearings, round gears, cams, bevel gears, various rollers, pulleys, pump impellers, fan blades, worm gears, thrusters, screws, nuts, gaskets, high-pressure sealing rings, oil resistant sealing gaskets, oil resistant containers, shells, hoses, cable sheaths, shears, pulley sleeves, shaper sliders, electromagnetic distribution valve seats, cold aging equipment, gaskets, bearing cages Various oil pipelines, pistons, ropes, transmission belts, zero fog materials for textile machinery and industrial equipment, daily necessities and packaging films on automobiles and tractors.
Product detail pictures:
Related Product Guide:
Gaining client pleasure is our company's aim without end. We are going to make excellent efforts to create new and top-quality goods, meet your special requirements and provide you with pre-sale, on-sale and after-sale companies for Newly Arrival Poe Resin - Fiber grade modified nylon PA6 Hunan Yuehua YH800 – TINCHAK , The product will supply to all over the world, such as: Serbia, Cologne, Bhutan, Due to the changing trends in this field, we involve ourselves into products trade with dedicated efforts and managerial excellence. We maintain timely delivery schedules, innovative designs, quality and transparency for our customers. Our moto is to deliver quality products within stipulated time.
By Josephine from Austria - 2018.11.28 16:25
Although we are a small company, we are also respected. Reliable quality, sincere service and good credit, we are honored to be able to work with you!
By Arabela from Bogota - 2018.02.08 16:45